Which stage of the fatigue crack is most significant in the low cycle fatigue?

Which stage of the fatigue crack is most significant in the low cycle fatigue? Correct Answer Crack growth on the plane of high tensile stress

The crack growth on the plane of high tensile stress or also called the stage-II of the crack growth is longest for the low cycle fatigue.

Related Questions

Which stage of the fatigue crack is most significant in the high cycle fatigue?
Consider the following statements regarding crack : 1. Crack is more likely to occur in the regions of discontinuity such as oil holes. 2. Crack is more likely to occur in the regions of irregularities in machining operations such as stamp mark. 3. Crack is more likely to occur in the internal cracks due to defects in materials like blow holes. Which of the above statements are correct ? 
The crack propagation rate with stress is given as ______ Where; -> da/dN is crack growth with each cycle -> C is constant -> σm is mean stress -> σa is alternating stress -> a is the crack length -> m and n are constant
The ductile material gives best result in the high strain amplitude or high cycle fatigue, while the strong material gives best result in high-stress low cycle fatigue.
There are 2 candidates A and B. Probability that A will crack the exam is 3/4 and that B will crack the exam is 2/3. What will be the probability that only one will crack the exam?
The young’s modulus of the steel is 600 MPa, and the plastic stress required to extend the crack is 50*10-9, and the initial crack length is 2 microns. Find the fracture stress required to crack the material?
According to Irwin’s correction of plasticity at the crack tip, the sufficient crack length is given as the actual crack length plus the radius of the plastic zone. The radius of the plastic zone (rp) in case of plane stress is given as ________
According to Irwin’s correction of plasticity at the crack tip, the effective crack length is given as the actual crack length plus the radius of the plastic zone. The radius of the plastic zone (rp) in case of plane strain is given as ________
Which code does not match? - Stage of Unification of Rajasthan Date (A) Third stage 18 April 1948 (B) Fourth stage 30 March 1948 (C) Fifth stage 15 May 1949 (D) Sixth stage 26 January 1950
Arrange the following steps of 'international product life cycle theory' in a correct order.
1. Maturity stage
2. Introductory stage
3. Decline stage
4. Growth stage