In slush casting, much of molten metal is wasted during the process of inverting mould.

In slush casting, much of molten metal is wasted during the process of inverting mould. Correct Answer False

The material does not get wasted in slush casting, instead this process saves a lot of molten metal by collecting it and that is reused for the other slushing steps. This process makes the casting lighter in weight by saving the molten metal; hence this process is good in an economical way.

Related Questions

A solid sphere has a radius 21 cm. It is melted to form a cube. 20% material is wasted in this process. The cube is melted to form hemisphere. In this process 20% material is wasted. The hemisphere is melted to form two spheres of equal radius. 20% material was also wasted in this process. What is the radius (in cm) of each new sphere?
A solid sphere has a radius 21 cm. It is melted to form a cube. 20% material is wasted in this process. The cube is melted to form hemisphere. In thisprocess 20% material is wasted. The hemisphere is melted to form two spheres of equal radius. 20% material was also wasted in this process. What is the radius (in cm) of each new sphere?
At the mould exit of a continuous caster, the metal consisting of a solidified shell with a liquid metal core exits at the rate of 35 kg S-1. Given that the latent heat of fusion is 3 × 105 J kg-1 and the total rate of heat removal by the mould is 4.2 × 106 W, the mass fraction of solid at the mould exit is . . . . . . . .
Assume that both while solid and liquid remain at the melting point, they are in the mould.
The casting processes that require expendable moulds are
P. Investment casting
Q. Low pressure casting
R. Shell moulding
S. Slush casting
In slush casting method, negligible metal loss is the main advantage during the casting process.
The riser is a reservoir of molten metal provided in the casting so that hot metal can flow back into the mould cavity when there is a reduction in the volume of metal due to?
The thickness of the metallic wall of the mould can be used to determine the wall thickness of the casting part in slush casting.
In permanent mould casting, the mould is pre-heated to its operating temperature before the actual use of mould.
Solidification time of a molten metal in a casting is proportional to (where, V = volume of metal & A = its surface area ; in the casting)
Solidification time of a molten metal in a casting is proportional to (where, V = volume of metal & A = its surface area; in the casting)