Molten metal is poured into the mould due to the effect of gravity with _______ external pressure in gravity die casting.

Molten metal is poured into the mould due to the effect of gravity with _______ external pressure in gravity die casting. Correct Answer No

Molten metal is poured into the mould under gravity only; no external pressure is applied to the force the liquid metal into the mold cavity. However, the liquid metal solidifies under pressure of metal in risers.

Related Questions

In vacuum die casting, the molten metal enters into the cavity slowly as compared to the die casting.
In low-pressure die casting, metal enters the mould very slowly as compared to the die casting.
The riser is a reservoir of molten metal provided in the casting so that hot metal can flow back into the mould cavity when there is a reduction in the volume of metal due to?
At the mould exit of a continuous caster, the metal consisting of a solidified shell with a liquid metal core exits at the rate of 35 kg S-1. Given that the latent heat of fusion is 3 × 105 J kg-1 and the total rate of heat removal by the mould is 4.2 × 106 W, the mass fraction of solid at the mould exit is . . . . . . . .
Assume that both while solid and liquid remain at the melting point, they are in the mould.
Molten metal is poured into the mould; meanwhile it removes the wax by melting it and vapourization of wax takes place simultaneously in the investment casting.
In vacuum die casting, the molten metal does not experience any back pressure while injecting it into the die cavity.
Water is poured into an empty cylindrical tank at a constant rate for 5 minutes. After the water has been poured into the tank. the depth of the water is 7 feet. The radius of the tank is 100 feet. Which of the following is the best approximation for the rate at which the water was poured into the tank ?
_________________ is a container which when poured with molten metal produce a casting of the shape of the mould.
In low-pressure die casting, mould is placed over the furnace containing the molten metal.
In vacuum die casting, the melt enters into the mould cavity with less speed than that in the die casting technique.