As per IS specifications, the maximum final setting time for ordinary Portland cement should be
A 30 minutes
B 1 hour
C 6 hours
D 10 hours
According to IS specifications, the compressive strength of ordinary Portland cement after three days should not be less than
A 7 MPa
B 11.5 MPa
C 16 MPa
D 21 MPa
Ordinary Portland Cement এর Initial Setting Time কত?
A ৫ মিনিট
B ১০ মিনিট
C ৩০ মিনিট
D ৫ ঘণ্টা
Alumina, silica, lime and iron oxide are the basic raw material for the manufacture of portland cement. The component of Portland cement which first hardens is
A 5CaO . 3Al2O3
B 3CaO . Al2O3
C 3CaO . SiO2
D 2CaO . SiO2
Initial setting time of cement for asbestos cement products should be not less than
A 30 minutes
B 50 minutes
C 75 minutes
D 90 minutes
As compared to ordinary portland cement, high alumina cement has
A Higher initial setting time but lower final setting time
B Lower initial setting time but higher final setting time
C Higher initial and final setting times
D Lower initial and final setting times
As compared to ordinary portland cement, use of pozzuolanic cement
A Reduces workability
B Increases bleeding
C Increases shrinkage
D Increases strength
The normal consistency of ordinary Portland cement is about
A 10%
B 20%
C 30%
D 40%
Addition of pozzolana to ordinary Portland cement increases
A Bleeding
B Shrinkage
C Permeability
D Heat of hydration
The main constituent of cement which is responsible for initial setting of cement is
A Dicalcium silicate
B Tricalcium silicate
C Tricalcium aluminate
D All of the above