As compared to ordinary portland cement, high alumina cement has
A Higher initial setting time but lower final setting time
B Lower initial setting time but higher final setting time
C Higher initial and final setting times
D Lower initial and final setting times
Alumina, silica, lime and iron oxide are the basic raw material for the manufacture of portland cement. The component of Portland cement which first hardens is
A 5CaO . 3Al2O3
B 3CaO . Al2O3
C 3CaO . SiO2
D 2CaO . SiO2
Ordinary Portland Cement এর Initial Setting Time কত?
A ৫ মিনিট
B ১০ মিনিট
C ৩০ মিনিট
D ৫ ঘণ্টা
The normal consistency of ordinary Portland cement is about
A 10%
B 20%
C 30%
D 40%
Addition of pozzolana to ordinary Portland cement increases
A Bleeding
B Shrinkage
C Permeability
D Heat of hydration
As per IS specifications, the maximum final setting time for ordinary Portland cement should be
A 30 minutes
B 1 hour
C 6 hours
D 10 hours
The initial setting time for ordinary Portland cement as per IS specifications should not be less than
A 10 minutes
B 30 minutes
C 60 minutes
D 600 minutes
According to IS specifications, the compressive strength of ordinary Portland cement after three days should not be less than
A 7 MPa
B 11.5 MPa
C 16 MPa
D 21 MPa
The addition of gypsum to portland cement helps in :
A Increasing the strength of cement
B Rapid setting of cement
C Preventing rapid setting of cement
D Reduction in the cost of cement
The compound of Portland cement which reacts immediately with water and also sets first is
A Tri-calcium silicate
B Di-calcium silicate
C Tri-calcium aluminate
D Tetra calcium alumino ferrite