The dislocation creep mechanism is active in the region ___________, where σ is applied stress and G is shear modulus.

The dislocation creep mechanism is active in the region ___________, where σ is applied stress and G is shear modulus. Correct Answer 10-4 < σ/G < 10-2

The mechanism involves the movement of dislocation, which overcomes barriers by a thermally assisted mechanism involving diffusion of vacancy or interstitial atoms. -> 10-4 < σ/G < 10-2.

Related Questions

What is the resolved shear stress, when dislocation density in metal is equal to 1012m-2? Given that shear stress needed in the absence of dislocation is 500MPa. Numerical constant is 0.3 and shear modulus is 80GPa, burger vector is 1 nm.
Tresca or maximum-shear stress criteria assumes that yielding occurs when the maximum shear stress reaches a value of the shear stress in the uniaxial tension test. Assume the principal stress being σ1, σ2, σ3 where σ1 is largest, and σ3 is the smallest principal stresses. Find the value of minimum shear stress to cause yielding, given that yield stress in tension is equal to σo?
Shear stress required to bend a dislocation of radius R and burger vector b is P. What will be shear stress needed to turn a dislocation of radius 2R and burger’s vector 2b to bend the dislocation?
Which of the following factors are affecting critical shear stresses? 1. Purity of metals reduces the critical shear stress 2. Surface films greatly enhance the critical shear stress 3. Rise in temperature 4. Rate of deformation and the extent of initial deformation also help in raising the critical shear stress
The following creep map is plotted with homologous stress and temperature, as shown in the region. The coble creep region is shown by region ________
The following creep map is plotted with homologous stress and temperature, as shown in the region. The Nabarro-Herring creep region is shown by region ________
The following creep map is plotted with homologous stress and temperature, as shown in the region. The Dislocation glide region is shown by region ________
The interaction of screw dislocation and edge dislocation produces ______ on the edge dislocation and _______ on the screw dislocation.
The Burgers vector b is the vector which defines the magnitude and direction of slip. For a pure edge dislocation, the Burgers vector is perpendicular to the dislocation line, while for a pure screw dislocation, the Burgers vector is parallel to the dislocation line.
The strain energy stored in a body due to shear stress, is (where $$\tau $$ = Shear stress, C = Shear modulus and V = Volume of the body)