Excess vacancies are retained during the quench if the age hardening alloys are retained from______

Excess vacancies are retained during the quench if the age hardening alloys are retained from______ Correct Answer High temperature

Excess vacancies are retained during the quench if the age hardening alloys are retained from high temperature. This can actually increase the diffusion rate or it can relieve the misfit strain energies hence it assist the nucleation.