Sodium fluosilicate added in the acid-resistant cement decreases the resistance of cement to water and acid and also retards the hardening process of soluble glass.

Sodium fluosilicate added in the acid-resistant cement decreases the resistance of cement to water and acid and also retards the hardening process of soluble glass. Correct Answer False

An acid-resistant cement consists of acid-resistant aggregates like quartz, additives like sodium fluosilicate and soluble glass. Sodium fluosilicate added in the acid-resistant cement increases the resistance of cement to water and acid and also accelerates the hardening process of soluble glass.

Related Questions

In a batch process, the reaction takes place in the presence of an acid medium. The acid is drained from the reaction vessel at the rate of 15ml/s as a result of the density difference of the acid from the reacting component. To avoid wastage of acid, it is recycled to an acid tank which has 1000 L capacity. The acid drained from the reaction vessel, picks up 50 g/L solids from the reactor. Acid is fed once again to the process from acid tank. When the process is started, the acid is almost pure in the tank as a result of filtration. As the reaction proceeds, acid in the tank gets more and more contaminated with the solids. The concentration of the solids should not exceed 100 g/L from the process point of view. The batch time is 16h. Estimate whether the concentration of the solids will exceed 100g/L during the batch reaction.
Match the following classification of glasses with their specific uses: a. Soda lime glass 1. Used in the manufacturing of glass articles which have to withstand high temperatures. b. Potash lime glass 2. Used in the manufacturing of artificial gems, electric bulbs, lenses, Prisms, etc. c. Potash lead glass 3. Used in the manufacturing of glass tubes, laboratory apparatus, plate glass, window panels, etc. d. Common glass 4. Used in the manufacturing of medicine bottles
There are two beakers with the first containing sodium hydroxide solution and the other beaker has twice the quantity of water. To prepare a solution, 60 ml of sodium hydroxide is added to the water beaker. Three fourth of the prepared solution is again added to the first beaker. After this the first beaker has 3.5 times the solution in the water beaker. How much was the initial amount of sodium hydroxide?
Measurement of KLa in a bioreactor can be carried out by sodium sulfite oxidation method, that is, based on the oxidation of sodium sulfite to sodium sulfate in the presence of a catalyst (Cu++ or Co++). In a typical experiment, a laboratory fermenter was filled with 5 liter of 0.5 M sodium sulfite solution containing 0.003 M Cu++ ions and the air was sparged in. After 10 min, the air flow was stopped and a 10 mL sample was taken and titrated. The concentration of sodium sulfite in the sample was found to be 0.20 M. The oxygen uptake rate for this aerated system will work out to be
A laboratory teacher had 1.5 litres of concentrated sulfuric acid. She replaces concentrated sulfuric acid with water after every class till the carton is empty. One student needs 10 ml of sulfuric acid mixture in every class. First class had 20 students and since then all other classes observed 10 students. Calculate total quantity of water with which mixture of sulfuric acid and water is replaced till carton is empty. Note 1.5 litres of concentrated sulfuric acid had 90% sulfuric acid and rest water
Consider the following statements: 1) Hydrophobic cement grains possess the low wetting ability 2) Rapid-hardening cement is useful in concreting under static, or running water 3) Quick-setting cement helps the concrete to attain high strength in the initial period 4) White cement is just a variety of ordinary cement-free of coloring oxides. Which of the above statements are correct?
Each of the two vessels X and Y has 20 litres of a solution of milk and water. X has 10% of water and certain quantity of water is added to it so as to raise the percentage of water to 25%. Y has milk and water in the ratio 3 : 2 and a certain quantity of water is added to this so as to reverse this ratio. What is the difference between the quantity of water added to X and that added to Y?
In a 60 litre solution of acid and water, the ratio of acid and water is 3 : 7. How much (in litre) acid is to be mixed in the solution so that the ratio of acid and water in the ration of acid and water in the resulting solution is 1 : 2?
Consider the following statements regarding 'setting of cement': 1. Low-heat cement sets faster than OPC. 2. Final setting time decides the strength of cement. 3. Initial setting time of Portland PozzoIlona is 30 minutes. 4. Air-induced setting is observed when stored under damp conditions. 5. Addition of gypsum retards the setting time. Which of the above statements are correct?
Consider the following statements.
1. Glass wool has tensile strength greater than steel.
2. Glass wool is fire proof.
3. Glass wool has high electrical conductivity and absorbs moisture.
4. Glass wool is used to prepare libre glass.
Which of the statements given above are correct?