Carburisation is a heat treatment used for case hardening steels. Carbon is trapped on steel surface by:

Carburisation is a heat treatment used for case hardening steels. Carbon is trapped on steel surface by: Correct Answer Interstitial diffusion

Carbon forms interstitial carbides with iron due to the large difference in atomic radii.

Related Questions

The only suitable method for hardening the low carbon steel is case hardening. Which of the following is a case hardening process?
Consider the following statements: 1. The quenching of steel results in an increase in wear resistance, strength and hardness. 2. By the process of case hardening, hard wearing resistant surface is produced on mild steel. This is an effective method for low carbon steels because they cannot be hardened by the process of quenching. 3. When a metal is mixed with small atoms of non-metallic element in such a manner that invading atoms occupy interstitial positions in the metal lattice, an interstitial alloy results. What of the above statements are correct?
Combined carbon content in iron and steel is determined by treating the sample with dilute HNO3. So that combined carbon forms a soluble brown nitrated compound, the intensity of which is matched with that of a standard sample of similar composition treated under similar condition. The intensity of color produced is proportional to the carbon content of iron of steel sample. This method of combined carbon determination is called the
A finned surface consists of root or base area of 1m2 and fin surface area of 2m2. The average heat transfer coefficient for finned surface is 20W/m2K effectiveness of fins provided is 0.75. If finned surface with surface with root or base temperature of 50°C is transferring heat to fluid of 30°C, then the rate of heat transfer without using fin is _______
Steel will respond to hardening by heat treatment processes, only when the minimum carbon content in it is __________ percent.
A Carnot heat engine receives heat at 750 K and rejects the waste heat to the environment at 300 K. The net work output of the heat engine is used to drive a Carnot refrigerator, whose COP is 6.14. If the heat removal rate from the refrigerated space is 6.6 kW, determine the rate of heat supply to the heat engine?
In the following question, the 1st and the last part of the sentence/ passage are numbered 1 and 6. The rest of the sentence/passage is split into four parts and named P, Q, R and S. These four parts are not given in their proper order. Read the sentence/passage and find out which of the four combinations is correct. 1. Global warming is the rise in average surface temperature of the earth globally. P. It is caused by the greenhouse effect of increased level of greenhouse gases. Q. Deforestation also increases carbon dioxide emissions. R. Greenhouse gases include carbon dioxide, CFCs, etc. S. The increasing use of fossil fuels is a major cause of carbon dioxide emission. 6. Carbon dioxide traps heat and causes the greenhouse effect.
In industries titanium is hardened through diffusion of carbon. The concentration of carbon at 1mm into the surface of the titanium slab is 0.25kg/m3 and at 3mm the concentration is 0.68kg/m3. The rate at which the carbon is entering into its surface is 1.27*10-9kg/m2.s. calculate the value of diffusion coefficient of carbon.
For hardening alloy steels and high speed steels, they are heated to
Consider the following statements: 1. Heat treatment is effective only in case of certain alloys. 2. Cooling rate is an important factor in any heat treatment process. 3. The temperature at which the change starts on heating the steel is called lower critical temperature. Which of the above statements are correct?