The two surfaces of a 5 mm thick plate of carbon steel are maintained at a carbon concentration of 104 mol. m-3 on one side and zero concentration on the other side. Taking the diffusion coefficient of carbon in austenite to be 10-11 m-2.s-1, the steady state flux (mol.m-3.s-1) through the thickness of the steel is

The two surfaces of a 5 mm thick plate of carbon steel are maintained at a carbon concentration of 104 mol. m-3 on one side and zero concentration on the other side. Taking the diffusion coefficient of carbon in austenite to be 10-11 m-2.s-1, the steady state flux (mol.m-3.s-1) through the thickness of the steel is Correct Answer 2 × 10<sup>-5</sup>

Related Questions

To effect a bond between two metal plates, 2.5 cm and 15 cm thick, heat is uniformly applied through the thinner plate by a radiant heat source. The bonding must be held at 320 K for a short time. When the heat source is adjusted to have a steady value of 43.5 k W/m2, a thermocouple installed on the side of the thinner plate next to source indicates a temperature of 345 K. Calculate the temperature gradient for heat conduction through thinner plate. In the diagram, the upper plate is 2.5 cm thick while the lower is 15 cm thick.
A composite slab consists of 5 cm thick layer of steel (k = 146 kJ/m hr degree) on the left side and a 6 cm thick layer of brass (k = 276 kJ/m hr degree) on the right hand side. The outer surfaces of the steel and brass are maintained at 100 degree Celsius and 50 degree Celsius. The contact between the two slabs is perfect and heat is generated at the rate of 4.2 * 10 5 k J/m2 hr at the plane of contact. The heat thus generated is dissipated from both sides of composite slab for steady state conditions. Calculate the temperature at the interface
The concentration of oxygen at the inner surface of the vessel is maintained at a level C depending on the pressure in the vessel, while the concentration at the outer surface is reduced to zero by the escape of oxygen to the surroundings. A steady state will eventually be reached when the concentration everywhere reaches a constant value. Provided D is independent of concentration there will be a single concentration gradient in the wall and the thickness of the wall is L, the flux is given by________________
Concentration of hydrogen gas across a 2mm thick palladium sheet differs by 4 kg/m3. Considering steady-state diffusion with diffusion constant 10-10 m2/s, diffusion flux is ______ kg/m2.s:
In a gas mixture of hydrogen and oxygen, steady state equimolar counter diffusion is occurring at a total pressure of 100 kPa and temperature of 20°C. If the partial pressures of oxygen at two planes 0.01 m apart, and perpendicular to the direction of diffusion are 15 kPa and 5 kPa, respectively and the mass diffusion flux of oxygen in the mixture is 1.6 * 10–5 kmol/m2.sec, calculate the molecular diffusivity for the system. For equimolar counter current diffusion:
A steel specimen containing 0.2 wt.% C is carburized in an atmosphere that maintains a carbon content of 1.2 wt.% C at the surface of the specimen.
Given:
For carbon diffusion in austenite: D0 = 2.0 × 10-5 m2/s
Activation energy for diffusion, Q = 142 kj/mol
In industries titanium is hardened through diffusion of carbon. The concentration of carbon at 1mm into the surface of the titanium slab is 0.25kg/m3 and at 3mm the concentration is 0.68kg/m3. The rate at which the carbon is entering into its surface is 1.27*10-9kg/m2.s. calculate the value of diffusion coefficient of carbon.
A composite wall consists of two plates A and B placed in series normal to the flow of heat. The thermal conductivities are kA and kB and the specific heat capacities are CPA and CPB for plates A and B respectively. Plate B has twice the thickness of plate A. At steady state, the temperature difference across plate A is greater than that across plate B, when
A composite wall consists of two plates A and B placed in series normal to the flow of heat. The thermal conductivities are kA and kB and the specific heat capacities are CPA and CPB for plates A and B respectively. Plate B has twice the thickness of plate A. At steady state, the temperature difference across plate A is greater than that across plate B, when
Consider following data for bulk polymerization, with benzoyl peroxide as initiator. = 6 mol/m3 = 6.56*103 mol/m3 kp2/kt = 1.5*10-6 m3/ mol-s What is the initiator efficiency if initial rate of polymerization is 0.0256 m3/ mol-s benzoyl peroxide decomposes at a rate of 3.2* 10-6 m3/ mol-s-1?