Related Questions

Fusion of bauxite and __________ produces high alumina cement.
A Alum
B Limestone
C Coke
D Quartz
With increasing alumina content, the fusion point of high alumina refractories
A Increases
B Decreases
C Remains constant
D May increase or decrease ; depends on its alumina content
Maximum alumina content in high alumina refractory can be as high as __________ percent.
A 30
B 50
C 70
D 90
Pure bauxite is the best raw material for the manufacture of high alumina refractories, in which maximum alumina content can be as high as __________ percent.
A 55
B 70
C 80
D 90
With increase in the alumina content, the refractoriness of high alumina refractories
A Increases
B Decreases
C Remains same
D May increase or decrease
As compared to ordinary portland cement, high alumina cement has
A Higher initial setting time but lower final setting time
B Lower initial setting time but higher final setting time
C Higher initial and final setting times
D Lower initial and final setting times
Alumina, silica, lime and iron oxide are the basic raw material for the manufacture of portland cement. The component of Portland cement which first hardens is
A 5CaO . 3Al2O3
B 3CaO . Al2O3
C 3CaO . SiO2
D 2CaO . SiO2
K produces 100 parts twice as fast as G does. G produces 100 parts in 40 minutes. If each produces parts at a constant rate, how many parts will K produces in 6 minutes.
A 30
B 25
C 20
D 15
With increase in the alumina content in firebricks, its fusion point (refractoriness)
A Decreases linearly
B Remains unchanged
C Increases
D Decreases
Production of one ton of cement requires about __________ tons of limestone.
A 0.6
B 1.2
C 2.2
D 3.8