The brittle material is extruded in the hydrostatic pressure extrusion process. Whereas ductile metal can be extruded through normal operations.

The brittle material is extruded in the hydrostatic pressure extrusion process. Whereas ductile metal can be extruded through normal operations. Correct Answer True

The hydrostatic pressure extrusion does not apply excessive force on any one side of the component, so it increases the ductility of the material. Therefore, the brittle material can be extruded without breaking the workpiece.

Related Questions

The extrusion ratio for hot extrusion is much more than the extrusion ratio for cold extrusion.
If the effective flow stress for extrusion is 100 MPa and the extrusion ratio is 4, then find the ideal extrusion pressure for the process?
The pressure required to maintain flow during indirect extrusion
P. decreases with decreasing rate of the billet
Q. Increases with increasing extrusion ratio
R. is independent of the length of the billet
S. is independent of the extrusion ratio
A round billet made of 70-30 brass is extruded at a temperature of 675°C. The billet diameter is 125 mm, and the diameter of the extrusion is 50 mm. Calculate the extrusion force required.
For ductile material to cause shearing, the penetration of tool along the thickness should be _____ whereas for brittle material it is ________
Statement A: Garden hose is an example of positive hydrostatic pressure. Statement B: Suction through straw is an example of negative hydrostatic pressure.
In hydrostatic testing of welded pipe (for leakage, strength etc.) the ratio of minimum hydrostatic test pressure to internal design pressure is around
Across the normal shockwave: 1) Stagnation pressure decreases whereas stagnation temperature remains constant 2) Mach number before the shockwave is always greater than one and after the shockwave, the Mach number need not be less than one 3) Across the shockwave there is a rise in pressure and temperature 4) The product of Mach number downstream of normal shockwave and upstream of normal shockwaves always one Which of the above statements are correct?
Find the extrusion pressure for the metal having extrusion constant 5*109. The initial and final cross-sectional area is 50 mm2 and 10 mm2?
If the extrusion ratio of the material used is increased by two times, the required extrusion pressure _____________