The elastic after effect is the decay of strain to zero with time after releasing the load on material.

The elastic after effect is the decay of strain to zero with time after releasing the load on material. Correct Answer True

The anelastic behavior of the material is termed as the delay in the strain recovery with time. This behavior is known as the elastic after effect.

Related Questions

From an alloy, two specimens are machined and tested separately under tension and compression. The engineering stress-strain curves as well as the true stress-true strain curves for tension and compression are plotted in the same diagram. Identify the correct statements:
P. The engineering stress-strain curves in tension and compression are identical.
Q. The true stress-true strain curve in compression is lower than the true stresstrue strain curve in tension due to Bauschinger effect.
R. The true stress-true strain curve in tension is above the corresponding engineering stress-strain, curve.
S. The true stress-true strain curve in tension and compression are identical.
Elastic failure of a material occurs, when the tensile stress equals yield strength, yield point or the elastic limit. Also, the elastic failure occurs according to maximum strain theory, when the maximum tensile strain equals (where, σ = yield strength and E = modulus of elasticity)
Elastic failure of a material occurs, when the tensile stress equals yield strength, yield point or the elastic limit. Also, the elastic failure occurs according to maximum strain theory, when the maximum tensile strain equals (where, $$\sigma $$ = yield strength and E = modulus of elasticity)
The following flow curve shows the deformation behavior of the material in the plastic region. The material is deformed till ε1 and released; the material immediately reached to strain ε2. And the time strain reached to ε3. So, there is a delayed recovery of strain. This is behavior of material is called _________
Three elastic constants for a completely anisotropic elastic material which follows the Hooke's law are young's modulus, elastic limit stress and yield stress. Which of the following properties is most sensitive to increase in strain rate ?
The true strain rate is given as ϒ, and conventional strain rate is given as ε. The engineering strain is equal to e. The relationship between conventional strain rate and true strain rate is _______
Consider the following statements: Dispatching authorizes the start of production operation by 1. releasing of material and components from stores to the first process 2. releasing of material from process to process 3. issuing of drawing and instruction sheets Which of the above statements are correct?
Which of the following statement regarding radioactive decay is correct?  Average life equals to 1.44 of half-life. Half-life is directly proportional to decay constant. The decay of element is proportional to no of atoms or moles.
Match the items in column 1 and column 2 and choose the correct combination. Column 1 Column 2 A - Resilience 1 – Ability of the material to return to the original shape when load is removed B – Fatigue 2 – Capacity of a material to absorb energy elastically C – Stiffness 3 – Ability of material to absorb a certain amount of energy without failure D - Elasticity 4 – Resistance of the material to elastic deformation   5 – Failure of material at loads less than that at normal conditions  
Consider the following statement: 1. Initial load tests and routine load tests are carried out on test piles and working Piles, respectively. 2. In a pile load test, the allowable load can be taken equal to half the ultimate load at which the total settlement amounts to one-tenth of the pile diameter. 3. In a pile load test, the allowable load can be taken equal to two-thirds of the total toad which causes a plastic settlement of 6 mm. Which of the above statements are correct?