Assume that 5mm and 5mm are the unstressed interplanar spacing’s of matching planes in the α and ß phases respectively, the disregistry, or misfit between the two lattices (∆) is defined by__

Assume that 5mm and 5mm are the unstressed interplanar spacing’s of matching planes in the α and ß phases respectively, the disregistry, or misfit between the two lattices (∆) is defined by__ Correct Answer 0

If dα and dβ are the unstressed interplanar spacing’s of matching planes in the α and β phases respectively, the disregistry, or misfit between the two lattices (Δ) is defined by Δ = (dα –dβ)/dα, here since the interplanar spacing’s are same, the misfit will be 0.

Related Questions

A spacing ‘’D’’ can be used to completely accommodate the lattice misfit in the one direction without any long-range strain field by a set of edge location. Calculate the value of D if the interplanar spacing’s of matching planes are given as 20mm, 19mm respectively? (Assume the misfit to be very small)
All the forms of matter except gases emit electromagnetic radiation continuously. The gases which electrically or thermally excited emit a certain wavelength only, then which of the following is/are true about the process (i) The spacing between the atoms in the other forms of matter is high than in gas (ii) The spacing between the atoms in gases is high than the other forms of matter (iii) The energy of the emitted radiation depends on the spacing between the atoms (iv) The wavelength of the emitted radiation depends on the spacing between the atoms 
The interplanar spacing of (220) planes of a FCC structure is 1.7458 Å. Calculate the lattice constant.
If d is the inter-planar spacing of the planes {h k I}, the inter-planar spacing of the planes {nh nk nl}, n being an interger, is
In a cubic crystal, atoms of mass M1 lie on one set of planes and atoms of mass M2 lie on planes interleaved between those of the first set. If C is the forte constant between nearest neighbour planes, the frequency of lattice vibrations for the optical phonon branch with wave vector k = 0 is
How many space lattices does the Bravais lattices consist of?
For an FCC metal, the ratio of interplanar spacing obtained from the first two peaks of the X-ray diffraction pattern is
Minimum interplanar spacing required for Bragg’s diffraction is:
Calculate the spacing of 5mm wires having a loss ratio of 0.075, compressive stress is 10.75n/mm2, 5mm diameter wires stress is 1000n/mm2, 12 wires of 8mm diameter are stressed to 1200n/mm2(Nd = 840n/mm2)?
The growth rate of pearlite, v, and the interlamellar spacing S are given by the following relation, $$v = k.\frac{1}{S}\left( {\frac{{1 - {S_c}}}{S}} \right)$$    where Sc is the critical spacing at which the growth rate is zero and k is a materials constant. The actual interlamellar spacing observed will correspond to