Which of the following is/are the factors that influence corrosion fatigue?

Which of the following is/are the factors that influence corrosion fatigue? Correct Answer Type of metal, corrosive solution composition, and temperature

The factors that influence corrosion fatigue: • Type of metal (FCC, BCC, HCP) • Composition of corrosive solution • Temperature • PH of the environment • Percentage of oxygen content.

Related Questions

S1: The exact cause of migraine is still not known.
P: Several factors like digestive disorders and psychological disturbances, have been said to be causative factors.
Q: Certain foods like cheese, chocolate or red wine have also been found to trigger off an attack.
R: The causative factors are numerous : psychologically, anxiety and frustration play an important part.
S: It seems to be hereditary and a majority of sufferers are women.
S6: On the other hand physical overexertion, fatigue, irregularities in dietary habits, prolonged eye strain are common precipitating factors.

The Proper sequence should be:
Corrosion of less corrosion-resistant metal is usually increased and the attack of the more corrosion-resistant is decreased in galvanic corrosion.
If the number of perfect square factors and perfect cube factors of 3000 is x and y respectively, then what is the ratio of the sum of total perfect square factors and the perfect cube factors to that of the total number of factors of 3000? Session Expired We will redirect you to login 1page in 5 secs. Please login again and resume your work
A material is a fatigue tested below the fatigue limit for few millions of cycles and then retested at higher than fatigue limit. This process is known as ___________
If the sample is tested for a large number of cycles below its fatigue limit and the stress is gradually increased above the fatigue limit, the true fatigue limit of material will _______
Corrosion fatigue is defined as the reduction of fatigue resistance due to the presence of a corrosive medium.
The number of pits generated on the surface of the material under fatigue corrosion are ________ than the number of pits on the surface of the same sample when it is tested only under corrosion environment.
Consider a reinforcing bar embedded in concrete. In a marine environment this bar undergoes uniform corrosion, which leads to the deposition of corrosion products on its surface and an increase in the apparent volume of the bar. This subjects the surrounding concrete to expansive pressure. As a result, corrosion induced cracks appear at the surface of concrete. Which of the following statements is TRUE?
Consider the following statements regarding corrosion of ceramic material: 1. Ceramic materials are much better suited to withstand most of these environments for reasonable time periods than are metals. 2. Corrosion of ceramic materials generally involves simple chemical dissolution, in contrast to the electrochemical processes found in metals. 3. Ceramic materials are not frequently used because of their non-resistance to corrosion. Which of the above statements is/are correct?
Which of the following corrosion form is considered as the intermediate stage between uniform corrosion and complete corrosion resistance?