The only suitable method for hardening the low carbon steel is case hardening. Which of the following is a case hardening process?
A Cyaniding
B Sheardising
C Spherodising
D None of these
Which is false statement about case hardening? Case hardening is done by
A Electroplating
B Cyaniding
C Induction hardening
D Nitriding
A solid material shows case hardening properties while drying. Which of the following should be controlled to control the drying process?
A Flow rate of inlet air
B Relative humidity of outlet air
C Humidity of inlet air
D Temperature of the solid
Occurrence of 'case hardening' during drying of a high moisture solid cake __________ the drying rate.
A Increases
B Decreases
C Does not affect
D Exponentially increases
Case hardening is not done by
A Nitriding
B Hot dipping
C Electroplating
D Both B & C
Hardening of steel is not possible, unless it is heated __________ critical point.
A Above the highest
B Above the lowest
C Between the first & second
D Between the second & third
Hardening of steel is not possible unless it is heated __________ critical point.
A Above the highest
B Above the lowest
C Between the first & second
D Between the second & third
In a hardening process, the hypo-eutectoid steel is
A Heated from 30°C to 50°C above the upper critical temperature and then cooled in still air
B Heated from 30°C to 50°C above the upper critical temperature and then cooled suddenly in a suitable cooling medium
C Heated from 30°C to 50°C above the upper critical temperature and then cooled slowly in the furnace
D Heated below or closes to the lower critical temperature and then cooled slowly
In order to remove internal stresses produced by hardening the steel, the process usually adopted is
A Tempering
B Normalizing
C Annealing
D Spheroidizing
Induction hardening is the process of
A Hardening surface of work-piece to obtain hard and wear resistant surface
B Heating and cooling rapidly
C Increasing hardness throughout
D Inducing hardness by continuous process