In a lead-acid cell dilute sulfuric acid (electrolyte) approximately comprises the following

In a lead-acid cell dilute sulfuric acid (electrolyte) approximately comprises the following Correct Answer Three parts H<sub>2</sub>O, one part H<sub>2</sub>SO<sub>4</sub>

Bissoy MCQ

Related Questions

Solution-1 containing 30% sulfuric acid flowing at the rate 10 Kg/min combines with Solution-2 containing 20% sulfuric acid flowing at the rate 5 Kg/min, if their product is out at the rate 20 Kg/min what is the percentage of sulfuric acid in the product?
In a batch process, the reaction takes place in the presence of an acid medium. The acid is drained from the reaction vessel at the rate of 15ml/s as a result of the density difference of the acid from the reacting component. To avoid wastage of acid, it is recycled to an acid tank which has 1000 L capacity. The acid drained from the reaction vessel, picks up 50 g/L solids from the reactor. Acid is fed once again to the process from acid tank. When the process is started, the acid is almost pure in the tank as a result of filtration. As the reaction proceeds, acid in the tank gets more and more contaminated with the solids. The concentration of the solids should not exceed 100 g/L from the process point of view. The batch time is 16h. Estimate whether the concentration of the solids will exceed 100g/L during the batch reaction.
What is the number of moles in 650 mL of 98% (v/v) sulfuric acid solution if density of sulfuric acid is 1.83 g/cm3?
A stock solution of 12.0 M sulfuric acid is made available. What is the best procedure to make up 100. mL of 4.0 M sulfuric acid using the stock solution and water prior to mixing?
Sulfurous acid is a weak acid, while sulfuric acid is a much stronger acid because
The ampere-hour efficiency of a leadacid cell is normally between
A strip of cupric acid paper, freshly moistened with a dilute solution of benzidine in dilute acetic acid is held in the pyrolytic vapours of polymer A and a bright blue colouration is obtained. Which of the following could be polymer A?
In case of an automobile battery, following are the reasons which will cause a defect of
1. Very high charging rate
2. High specific gravity of electrolyte
3. Freezing of electrolyte
4. Improper level of electrolyte
5. Mechanical damage due to rough handling or not fixed in the vehicle
The oxygen activity in a liquid metal can be-measured by a concentration cell using stabilised zirconia electrolyte PO2(1) | ZrO2 based solid electrolyte | PO2(2)
Where, PO2(1) is the reference oxygen pressure and PO2(2) is the oxygen pressure in equilibrium with liquid metal. If, F is Faraday constant, the EMF of the cell is equal to
Which of the following factors adversely affects the capacity of the leadacid battery ?