What is the type of welding defect caused due to shrinkage during solidification and by weld stresses called?

What is the type of welding defect caused due to shrinkage during solidification and by weld stresses called? Correct Answer Lamellar tearing

Lamellar tearing is a cracking phenomenon, which occurs beneath welds, and is principally found in rolled steel plate fabrications. The tearings always lies within the parent plate, often outside the transformed (visible) heat- affected zone (HAZ), and is generally parallel to the weld fusion boundary.

Related Questions

Which of the following statement(s) is/are true regarding butt welding? 1. Flash butt welding is a combination of resistance, arc and pressure welding 2. Upset butt welding is used for welding rods 3. Percussion Welding is a self timing spot welding method 4. Aluminium alloys are flash welded
In the consumable electrode shielded metal arc welding process, which of the following observations are correct?
P. The, weld composition does not depend upon the basicity of the slag.
Q. Basic flux is used to achieve low hydrogen content-and low inclusion content in the weld metal.
R. Reverse polarity of the direct current power source is used to weld thin sheets.
S. Coated electrodes are classified by tensile strength of the weld metal deposit.
Which row of the following table correctly matches the terms with the respective processes of state-change?   Change of State   Gas to liquid Liquid to solid Solid to liquid 1. Condensation Melting Solidification 2. Condensation Solidification Melting 3. Evaporation Melting Solidification 4. Evaporation Solidification Melting
Which of the following statements are correct with reference to ensuring minimum shrinkage of prestressed concrete? 1. The water-cement ratio and proportion of cement paste should be kept minimum to reduce shrinkage. 2. Aggregates of larger size, well graded for minimum void, need a smaller amount of cement paste, and attendant shrinkage will be smaller. 3. Harder and denser aggregates of low water absorptions and high modulus of elasticity will exhibit small shrinkage.
A fillet-welded joint is subjected to transverse loading F as shown in the figure. Both legs of the fillets are of 10 mm size and the weld length is 30 mm. If the allowable shear stress of the weld is 94 MPa, considering the minimum throat area of the weld, the maximum allowable transverse load per weld in kN is
What is the type of welding defect caused due to poor deposition of weld rod is called?
What is the type of welding defect caused due to poor manipulation of weld rod or a dirty joint called?
What is the type of welding defect is caused due to stresses on heating and cooling called?
Consider the following statements in respect of the oxidizing flame due to excess oxygen in welding: 1) AT high temperature, it combines with many metals to form hard and brittle oxides. 2) It causes the weld bead and the surrounding area to have a scummy appearance 3) It has good welding effect in welding of copper-base metal. Which of the above statements are correct?
Shrinkage and weld stress in casting is responsible for which welding defect?