What is the monomer composition of polymer named Vamac?

What is the monomer composition of polymer named Vamac? Correct Answer methyl acrylate, ethylene, curing site monomer

A terpolymer of methyl acrylate, ethylene and a cure site monomer is known as Vamac in the trade.
Bissoy MCQ

Related Questions

A polymer ‘A’ is formed by the polymerization of monomer B. Monomer B is formed by the pyrolysis of monochlorodifluoromethane in contact with platinum at 700 ᵒC. Monomer is a highly crystalline polymer with excellent insulation properties. What is the name of monomer B?
Monomer A is reacted with a monomer B in boiling methanol to form a salt. The salt dissolved in water with a little amount of acetic acid is then processed in autoclave at different temperatures and pressure. Monomer A is a bifunctional monomer having amine groups. What is the name of monomer B?
The styrene radical is apparently 500-1000 times less reactive than the vinyl acetate monomer, and also the styrene monomer is 50-100 times less reactive than the vinyl acetate monomer. State true or false.
The simplest type of polymer is the _________ a polymer containing only 1 type of monomer.
What is the monomer composition of IIR polymer or Butyl Rubber?
Melt spinning of polymers involves the forcing of polymer melt through spinnerettes (fine holes) into an atmosphere kept at a temperature lower than the melting point of the polymer, which causes the fine diameter polymer melt to harden into filaments. Melt spinning is not used in case of the __________ fibres.
Polymer A, also available as copolymer with trifluoroethylene, is a crystalline polymer with a melting point greater than 160 ᵒC and is used in coatings and insulation materials. What is the name of polymer A?
A glass reinforced polymer composite comprises of 35 volume % glass fiber and 65 volume % of polymer resin. The elastic moduli of glass and polymer resin are respectively 70 GPa and 3 GPa. The elastic modulus of the composite (in GPa) under iso-strain state is
A monomer is dispersed in a solution of_________ and ____________ forming the relatively large droplets of monomer.
How is the degree of polymerization affected with the increase in concentration of both monomer and liquid ammonia, when a monomer is polymerized anionically in liquid ammonia?