Fatigue strength of iron and steel _________ with an increase in temperature.

Fatigue strength of iron and steel _________ with an increase in temperature. Correct Answer First increases and then decreases

Fatigue strength of materials increases with an increase in temperature above 100˚C. This value reaches a maximum value between 200˚C and 400˚C. After this decrease is seen.
Bissoy MCQ

Related Questions

Compared to mild steel, cast iron has
(i) High compressive strength
(ii) High tensile strength
(iii) Low compressive strength
(iv) Low tensile strength
Which of the following statements are true with respect to iron ore?
I. Limestone and coal are important for smelting iron ore
II. More than 20% of the world iron ore deposits are in India
III. Odisha and Jharkhand top in the production of iron ore
IV. Iran is the largest buyer of Indian iron ore
Out of the total production of iron from hematite, an ore of Iron, 20% of the ore gets wasted, and out of the remaining iron, only 25% is pure iron. If the pure iron obtained in a year from a mine of hematite was 80,000 kg, then the quantity of hematite mined from that mine in the year is
Consider the following statements
1. Galvanisation is the method of protecting steel and iron fromrusting by coating them with a thin layer of zinc.
2. Pure iron is very soft but if it is mixed with a small amount of carbon, it becomes hard and strong.
3. When iron is mixed with nickel and chromium, we get stainless steel, which is hard and does not rust.
Which of the statements given above are correct?
A material is a fatigue tested below the fatigue limit for few millions of cycles and then retested at higher than fatigue limit. This process is known as ___________
If the sample is tested for a large number of cycles below its fatigue limit and the stress is gradually increased above the fatigue limit, the true fatigue limit of material will _______
Which factor decreases the fatigue strength of iron and steel?
What causes an increase in fatigue strength of steel?
The yield point in fatigue loading compared to that in static loading is less. The ratio of ultimate tensile strength to endurance limit of a material subjected to fatigue loading is
Smaller the value of b (fatigue strength exponent) _____________ the fatigue life.