Stress during cracking _____ in ductile fracture and _____ in brittle.

Stress during cracking _____ in ductile fracture and _____ in brittle. Correct Answer Increases, constant

Stress during cracking increases in the ductile fracture. In brittle fracture, stress remains constant. It is due to no plastic deformation associated.

Related Questions

Brittle fracture needs more energy than the ductile fracture.
The brittle fracture is considered much more severe than ductile fracture.
The Ductile fracture depends strongly on strain rate compared with brittle fracture, which is relatively insensitive to strain rate.
Brittle fracture is more dangerous than ductile fracture because
Fracture stress for a brittle material having a crack lenght of 1μm is 200 MPa. Fracture stress for the same material having a crack lenght of 4 μm is
Consider the following statements for ductile fracture: 1. The material undergoes substantial plastic deformation with high energy absorption before fracture. 2. Presence of cracks on the surface of material initiates this type of failure. 3. Fracture occurs due to necking. Which of the above statements is/are correct? 
From an alloy, two specimens are machined and tested separately under tension and compression. The engineering stress-strain curves as well as the true stress-true strain curves for tension and compression are plotted in the same diagram. Identify the correct statements:
P. The engineering stress-strain curves in tension and compression are identical.
Q. The true stress-true strain curve in compression is lower than the true stresstrue strain curve in tension due to Bauschinger effect.
R. The true stress-true strain curve in tension is above the corresponding engineering stress-strain, curve.
S. The true stress-true strain curve in tension and compression are identical.
Brittle fracture is a break in a brittle piece of metal that failed because stress exceeds _____
The fracture stress according to Orowan’s theory of brittle fracture is __________ (where E is Yong’s modulus, ϒp is the plastic work required to extend the crack wall of the length 2
Strain energy required in a ductile fracture is ____ and _____ in brittle.