Stiffness and strength of polymer ___ with an increase in the degree of crystallinity.

Stiffness and strength of polymer ___ with an increase in the degree of crystallinity. Correct Answer increases

Higher degree of crystallinity gives a stiffer polymer. In semi crystalline polymer, strong intermolecular forces are found. These make polymer stiffer but also brittle.
Bissoy MCQ

Related Questions

Let D be a simple graph on 10 vertices such that there is a vertex of degree 1, a vertex of degree 2, a vertex of degree 3, a vertex of degree 4, a vertex of degree 5, a vertex of degree 6, a vertex of degree 7, a vertex of degree 8 and a vertex of degree 9. What can be the degree of the last vertex?
For stable structures, one of the important properties of flexibility and stiffness matrices is that the elements on the main diagonal
(i) Of a stiffness matrix must be positive
(ii) Of a stiffness matrix must be negative
(iii) Of a flexibility matrix must be positive
(iv) Of a flexibility matrix must be negative
The correct answer is
The rear window of an automobile is made of thick glass i.e. AB = 5 mm and thermal conductivity is 0.8 W/m degree. To defrost this window, a thin transparent film type heating element has been fixed to its inner surface. For the conditions given below, determine the electric power that must be provided per unit area of window if a temperature 5 degree Celsius is maintained at its outer surface. Interior air temperature and the corresponding surface coefficient are 20 degree Celsius and 12 W/m2 degree. Surrounding air temperature and the corresponding surface coefficient are – 15 degree Celsius and 70 W/m2 degree. Electric heater provides uniform heat flux
Which of the following property of a polymer decreases with an increase in crystallinity?
There are blank spaces in the following passage which have been numbered . These numbers are printed below the passage and against each some words are suggested . Find out the word that best fit the blank spaces. Global Strategies to control infective disease have historically included the erection of barriers to international travel and ___ (24) _______. Keeping people with such deadly disease outside national borders has ___ (25) _______ as an important public health policy in the human immunodeficiency virus (HIV) epidemic . Betwwn 29 and 50 countries ___ (26) _____ to have introduced border restrictions on HIV _ positive foreigners ,usually those planning an ___ (27) ___ stay in the country , such as students , workers or seamen.
The capacity of a material to absorb energy depends upon both its strength & stiffness. The term 'stiffness' of a material is the opposite of its
During heat treatment, cylindrical pieces of 25 mm diameter, 30 mm height and at 30 degree Celsius are placed in a furnace at 750 degree Celsius with convective coefficient 80 W/m2 degree. Calculate the time required to heat the pieces to 600 degree Celsius. Assume the following property values Density = 7850 kg /m3 Specific heat = 480 J/kg K Conductivity = 40 W/m degree
A water line is buried underground in dry soil that has an assumed initial temperature of 4.5 degree Celsius. The pipe may have no flow through it for long period of time, yet it will not be drained in order that no freezing occurs, the pipe must be kept at a temperature not lower than 0 degree Celsius. The pipe is to be designed for a 30 hour period at the beginning of which the soil surface temperature suddenly drops to – 17 degree Celsius. Workout the minimum earth covering needed above the water pipe so as to prevent the possibility of freezing during 36 hour cold spell. The soil in which the pipe is buried has the following properties Density = 640 kg/m3 Specific heat = 1843J/kg degree Thermal conductivity = 0.345 W/m degree
A glass reinforced polymer composite comprises of 35 volume % glass fiber and 65 volume % of polymer resin. The elastic moduli of glass and polymer resin are respectively 70 GPa and 3 GPa. The elastic modulus of the composite (in GPa) under iso-strain state is
Polymer A, also available as copolymer with trifluoroethylene, is a crystalline polymer with a melting point greater than 160 ᵒC and is used in coatings and insulation materials. What is the name of polymer A?