In which of the following casting method, the molten metal is poured and allowed to solidify while the mold is revolving?

In which of the following casting method, the molten metal is poured and allowed to solidify while the mold is revolving? Correct Answer centrifugal casting method

A casting process in which the molten metal is poured and allowed to solidify while the mold is revolving, is called centrifugal process. The casting produced under this centrifugal force is called centrifugal casting. This process is especially designed for a casting of symmetrical shape.
Bissoy MCQ

Related Questions

In a _______, the molten metal is poured and allowed to solidify while the mould is revolving.
In which of the following casting process, the metal being poured into the mold begins to solidify at ceramic walls?
A 250 mm by 250 mm ingot casting, 1.5 m high and at 1225 K temperature, is stripped from its mold. The casting is made to stand on end on the floor of a large foundry whose wall, floor and roof can be assumed to be at 300 K temperature. Make calculation for the rate of radiant heat interchange between the casting and the room. The casting material has an emissivity of 0.85
In which of the following casting technique, the molten metal is forced upward by gas pressure into a graphite or metal mold?
The process in which molten metal flows by gravity or other force into a mold where it solidifies in the shape of the mold cavity is known as_____
In the casting of steel under certain mold condition the mold constant in Chvorinov’s rule is known to be 4 min/cm2.The volume and the surface area of the casting plate is known to be 600cm3 and 760cm2 respectively. Calculate the solidification time?
Two square shaped steel plates A and B have thickness of 4 and 8 cms respectively. They are sand cast under identical conditions. Plate A takes 10 minutes to solidify. Plate B would solidify in . . . . . . . . minutes.
Water is poured into an empty cylindrical tank at a constant rate for 5 minutes. After the water has been poured into the tank. the depth of the water is 7 feet. The radius of the tank is 100 feet. Which of the following is the best approximation for the rate at which the water was poured into the tank ?
Molten metal is poured into the mould; meanwhile it removes the wax by melting it and vapourization of wax takes place simultaneously in the investment casting.
In which type of casting, molten metal is poured into moulds which keep on rotating?